Extreme pressure (EP) additives − the other metal guardians in your oil additives − work their magic under pressure. These are sulphurised fats and oils, organic sulphur compounds, sulphides, phosphates, metal dithiophosphates and chlorine compounds.
They reduce friction and wear and prevent scoring and seizure. This is done through a chemical reaction with the metal surface that forms a film with lower shear strength than the metal, thereby preventing metal-to-metal contact.
EP additives work their magic at the beginning of the Stribeck Curve, where lubrication conditions are either in the mixed-lubrication or boundary-lubrication regimes. However, EP additives are generally more critical in boundary-lubrication conditions than in mixed lubrication.
In boundary-lubrication conditions, the interacting surfaces are in direct contact without a sufficient oil film separating them. EP additives play a crucial role by preventing adhesive wear and protecting components when the lubricating oil is unable to maintain an adequate film thickness. They are activated at high loads and by the high contact temperatures that are created in boundary-lubrication conditions. They are typically used in gear oils and give those oils that unique, strong sulphur smell.
These additives are more chemically aggressive than anti-wear additives. They react chemically with metal (iron) surfaces to form a sacrificial surface film that prevents the welding and seizure of opposing asperities caused by metal-to-metal contact (adhesive wear).
Let’s look at the common types of EP additives.
Sulphur-based compounds form metal sulphide films, and are among the most widely used and effective EP additives. They rely on tribochemical reactions to create these protective metal sulphide films. Under high pressure between metal surfaces, the sulphur bonds in the additives break, releasing reactive sulphur. This sulphur then reacts with metal atoms to form metal sulphides, which have a layered crystalline structure. This structure creates a lubricating film with high adhesion, low shear-strength, and the ability to replenish rapidly as it wears away.
Sulphur-based EP additives can be categorised into two types:
• Active sulphur EP additives: these are highly reactive and readily interact with metal surfaces, especially at elevated temperatures. They form a protective metal sulphide film that prevents metal-to-metal contact under extreme pressure. However, active sulphur can also cause corrosion of softer metals, such as copper and brass.
• Inactive sulphur EP additives: these are less reactive at typical operating temperatures and do not aggressively attack metal surfaces. They provide EP protection by gradually forming protective layers through slower chemical reactions, without aggressively bonding with the metal surface under standard conditions.
Phosphorus-based compounds form metal phosphate films, creating a smooth polyphosphate layer that offers good wear resistance and load-bearing capacity. While these films are typically thicker, they are less durable than sulphur-based films and may have reduced effectiveness at higher temperatures.
Chlorine-based compounds form iron chloride films, but the use of these additives has significantly declined due to toxicity concerns.
EP additives protect load-bearing surfaces through a series of reactions over the oil’s lifecycle. The process generally involves the following key steps:
• Adsorption: Additive molecules are attracted to metal surfaces through polar interactions.
• Tribochemical reaction: Under extreme pressure, the additive molecules decompose and chemically react with the metal surface, forming a protective, inorganic compound.
• Film formation: Depending on the type of EP additive, the reaction products form a smooth protective layer, which may be crystalline or amorphous in structure. This film reduces friction and metal-to-metal contact, providing a smooth, lubricating film to protect surfaces under high pressure.
• Shock load absorption: The protective film, whether crystalline or amorphous, absorbs pressure spikes and helps reduce mechanical stress on the base-oil film, preventing metal-to-metal contact.
• Regeneration: As the protective films wear off, the additives in the oil regenerate the film, maintaining ongoing protection.
The exact chemical reactions between the additive and metal depend on both the type of EP additive and the composition of the base metal, but in essence, EP additives sacrifice themselves to form inorganic solid films on the metal surface that deliver wear protection under boundary-lubrication conditions. They’re the true specialists in boundary conditions; chemically reactive, mechanically effective, and always ready to shine when the pressure is on.
| Tel: | +27 31 700 5460 |
| Email: | [email protected] |
| www: | www.wearcheck.co.za |
| Articles: | More information and articles about Wearcheck |
© Technews Publishing (Pty) Ltd | All Rights Reserved
printer friendly version